Degradation of the main gas pipeline material and mechanisms of its fracture

    Pavlo Maruschak Affiliation
    ; Iryna Danyliuk Affiliation
    ; Olegas Prentkovskis Affiliation
    ; Roman Bishchak Affiliation
    ; Andriy Pylypenko Affiliation
    ; Andriy Sorochak Affiliation
DOI: https://doi.org/10.3846/13923730.2014.971128

Abstract

The effect of the in-service scattered damage in the pipe wall metal is evaluated, and the effect of hydrogen absorbed by metal on the variation of the structure and mechanical properties of the main gas pipeline after a long-term operation is found. The main regularities in the graded nature of the static deformation process and the effect of hydrogenation on the scattered damage and fracture accumulation are found.

Keyword : fracture, failure, structural damage, strain localisation, hydrogenation, degradation, gas pipeline

How to Cite
Maruschak, P., Danyliuk, I., Prentkovskis, O., Bishchak, R., Pylypenko, A., & Sorochak, A. (2014). Degradation of the main gas pipeline material and mechanisms of its fracture. Journal of Civil Engineering and Management, 20(6), 864-872. https://doi.org/10.3846/13923730.2014.971128
Published in Issue
Dec 20, 2014
Abstract Views
651
PDF Downloads
400
Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.