Research of technological properties of steel X6CrNiTi18-10 welded joints exploited in nitric acid medium

Abstract

The repair of chemical industry equipments often requires to replace long time operated pipes or welded inserts with the simi-lar chemical composition. During the study the joints from corro-sion resistant steel X6CrNiTi18-10 were welded by manual metal arc welding with covered electrodes (MMA process 111) and tungsten inert gas welding (TIG process 141) at different welding parameters. The visual, radiographic, penetrant control and ferrite content analysis were carried out. The transverse tensile and bending samples were produced from welded samples; also the macroscopic and microscopic analyse were carried out.

Article in Lithuanian.

Plieno X6CrNiTi18-10, eksploatuojamo azoto rūgšties terpėje, virintinių jungčių technologinių savybių tyrimas

Santrauka 

Atliekant chemijos pramonės įrenginių remontą, dažnai tenka pakeisti ilgą laiką eksploatuotus vamzdžius ar įvirinti analogiškos cheminės sudėties intarpus. Tyrimo metu suvirintų jungčių bandomieji pavyzdžiai iš korozijai atsparaus plieno X6CrNiTi18-10 buvo suvirinti rankiniu lankiniu būdu glaistytaisiais elektrodais (111 MMA procesas) ir lankiniu suvirinimu volframo elektrodu inertinėse dujose (141 TIG procesas), esant skirtingiems suvirinimo režimų parametrams. Suvirintiems bandiniams buvo atlikta vizualinė, radiografinė, spalvinė kontrolė, nustatytas išsiskyrusio ferito kiekis. Iš suvirintų ruošinių buvo pagaminti skersinio tempimo, lenkimo bandiniai, taip pat atlikti virintinių jungčių makroskopinis ir mikroskopinis tyrimai.

Raktiniai žodžiai: chromnikelinis plienas, suvirintos jungtys, korozija, neardomoji kontrolė, mechaniniai bandymai.

Keyword : chromium-nickel steel, welded joints, corrosion, non-destructive control, mechanical tests